Polyamide Raw Resin PA6 Material Granule Virgin Nylon PA6 GF30 Plastic Granules

• CAS No.: ISO9001:2008.RoHS
• Material: Polyamide(Nylon 6.66)/PA
• Usage: General Plastics, Engineering Plastics, Specialty Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Film Pressure
• Transport Package: Plastic Bag Packaging
• Model NO.: pa6
• Specification: 5*5mm
• Origin: China
• Production Capacity: 25kgs/Bag

Product Description

 

Basic Info.

Plastic Forming Method	Injection	Color	White
Shape	Granular	Quality	Stable
ODM/OEM	Accept	Grade	Injection Grade
Transport Package	25kg/Bag	Specification	65*40*15cm
Production Capacity	1000kgs/Week	Origin	China
HS Code	3908101101	port of loading	shanghai port

 

Product Description

Product features: High strength, high toughness, good heat resistance, low water absorption, good processability

 

Product Application: Engineering plastic particles, silk textile, fishing nets and fishing gear, new energy products and daily necessities,etc.

Polyamide Plastic Raw Materials Injection Grade Virgin Nylon pa6 30gf 

Product Description		Applications
· 30% glass fiber reinforced		· Injection molding
· superb heat stability		· Good mechanical properties balance
Properties	Test Method	Test Condition		Unit	Typical Values
Physical properties
Specific Gravity	ISO 1183	23ºC		g/cm3	1.35
Ash	ISO 3451	800ºC,30min		%	30
Mechanical properties
Tensile Strength	ISO 527	50mm/min		MPa	125
Elongation at Break	ISO 527	50mm/min		%	2.5
Flexural Modulus	ISO 178	2mm/min		MPa	8500
Izod Notched Impact Strength	ISO 180	23ºC		kJ/m2	9
Thermal properties
Heat deflection temperature	ISO 75	1.80MPa		C	185
Melting Point	DSC	-		C	222
Other properties
Mold Shrinkage	internal test method	48 hours after tool		%	0.3-0.5
Flammability	TL1010	-		mm/min	39
Note: The data above is a typical value for reference, not a guaranteed value. The data will vary with tool design such as gate type , gate location, gate number, injection molding process and part thickness. The data will vary with different color as well. Prior to use the material, please consult with Sunway polymer.
Processing Conditions			Range
Melt Temperature			240-270ºC
Barrel Temperature	Rear		240--250ºC
	Center		255--265ºC
	Front		260--270ºC
Mold Temperature			50-80ºC
Pre-Dry needed			100ºC, 4-8h
Note: The above process condition is only for reference. The actual process should be adjusted according to different types of machines,  mold design and product design.

 

Pictures Show

 

Company Information:ANHUI SINCERE EXPORT & IMPORT CO., LTD.

    Anhui Sincere Import and Export Co., Ltd. is located in Hefei, the capital of Anhui Province in China, science and technology innovation city, is responsible for the import and export subsidiary of Bravo-Han Group. 

 

more product

    We have more than 30 years of experience in plasticizing industry and trade, with specialized plasticizing research and development department and production lines. The core products are professional and rich plasticization product systems such as PA,PC,PE, POM,ABS etc. At the same time, it is involved in a wide range of plasticization product application fields such as high-speed spinning , fishing line/twine/thread, fishing net and gear, clothing, auto parts and injection molding industry. 

 

Certificate

 

FAQ