CAS No.: | ISO9001:2008.RoHS |
---|---|
Formula: | [-Hn(CH2)5co-]N |
Material: | Polyamide(Nylon 6.66)/PA |
Usage: | General Plastics, Engineering Plastics, Specialty Plastics |
Plastic Properties After Heated: | Thermoplastic Plastics |
Plastic Forming Method: | Film Pressure |
Samples: |
---|
Customization: |
---|
Suppliers with verified business licenses
Basic Info. |
Plastic Forming Method | Injection | Color | White |
Shape | Granular | Quality | Stable |
ODM/OEM | Accept | Grade | Injection Grade |
Transport Package | 25kg/Bag | Specification | 65*40*15cm |
Production Capacity | 1000kgs/Week | Origin | China |
HS Code | 3908101101 | port of loading | shanghai port |
Product Description |
Product features: High strength, high toughness, good heat resistance, low water absorption, good processability
Product Application: Engineering plastic particles, silk textile, fishing nets and fishing gear, new energy products and daily necessities,etc.
Product Description | Applications | ||||
· 30% glass fiber reinforced | · Injection molding | ||||
· superb heat stability | · Good mechanical properties balance | ||||
Properties | Test Method | Test Condition | Unit | Typical Values | |
Physical properties | |||||
Specific Gravity | ISO 1183 | 23ºC | g/cm3 | 1.35 | |
Ash | ISO 3451 | 800ºC,30min | % | 30 | |
Mechanical properties | |||||
Tensile Strength | ISO 527 | 50mm/min | MPa | 125 | |
Elongation at Break | ISO 527 | 50mm/min | % | 2.5 | |
Flexural Modulus | ISO 178 | 2mm/min | MPa | 8500 | |
Izod Notched Impact Strength | ISO 180 | 23ºC | kJ/m2 | 9 | |
Thermal properties | |||||
Heat deflection temperature | ISO 75 | 1.80MPa | C | 185 | |
Melting Point | DSC | - | C | 222 | |
Other properties | |||||
Mold Shrinkage | internal test method | 48 hours after tool | % | 0.3-0.5 | |
Flammability | TL1010 | - | mm/min | 39 | |
Note: The data above is a typical value for reference, not a guaranteed value. The data will vary with tool design such as gate type , gate location, gate number, injection molding process and part thickness. The data will vary with different color as well. Prior to use the material, please consult with Sunway polymer. | |||||
Processing Conditions | Range | ||||
Melt Temperature | 240-270ºC | ||||
Barrel Temperature | Rear | 240--250ºC | |||
Center | 255--265ºC | ||||
Front | 260--270ºC | ||||
Mold Temperature | 50-80ºC | ||||
Pre-Dry needed | 100ºC, 4-8h | ||||
Note: The above process condition is only for reference. The actual process should be adjusted according to different types of machines, mold design and product design. |